| Mechanical Characteristics |
| Tensile strength |
MPa |
ISO 527-1,2 |
115 |
| Tensile strain at break |
% |
6.0 |
| Tensile modulus |
GPa |
6.7 |
| Flexural strength |
MPa |
ISO 178 |
175 |
| Flexural modulus |
GPa |
5.8 |
| Charpy notched impact strength |
kJ/m2 |
ISO 179-1/1eA |
24 |
| Rockwell hardness |
R.Scale |
- |
ISO 2039-2 |
110 |
| M.Scale |
- |
| Thermal Characteristics |
| Melting temperature |
°C |
ISO 11357 |
175~181 |
| Coeff. of linear thermal expansion |
x10-5/°C |
ISO 11359-2 |
3.0 |
| Temperature of deflection under load |
0.45 MPa |
°C |
ISO 75-1,2 |
177 |
| 1.8 MPa |
°C |
161 |
| Electical Characterisitics |
| Volume resistivity |
Ωcm |
JIS K6911 |
1015 |
| Electric strength |
kV/mm |
IEC 60243-1 |
- |
| Relative permittivity |
- |
IEC 60250 |
- |
| Arc resitance |
s |
D-495(ASTM) |
- |
| Others |
| Density |
g/cm3 |
ISO 1183-3 |
1.24 |
| Water absorption |
23 °C, 50 %RH |
% |
UBE method |
- |
| Molding shrinkage |
MD |
% |
UBE method(30x100x3t) |
- |
| TD |
- |
| Nomenclature accdording to ISO 16396-1 |
|
|
PA12, GF30. M1HR, C18-060 |