| Mechanical property |
| Tensile strength |
MPa |
ISO 527-1,2 |
26 |
| Tensile strain at break |
％ |
>150 |
| Tensile modulus |
MPa |
450 |
| Flexural strength |
MPa |
ISO 178 |
19 |
| Flexural modulus |
MPa |
400 |
| Charpy notched impact strength |
kJ/m2 |
ISO 179-1/1eA |
115 |
| Rockwell hardness |
R.Scale |
- |
ISO 2039 |
51 |
| Shore D hardness |
- |
ISO 868 |
67 |
| Thermal property |
| Melting temperature |
℃ |
ISO 11357 |
170～176 |
| Temperature of deflection under load |
0.45 MPa |
℃ |
ISO 75-1,2 |
91 |
| 1.8 MPa |
45 |
| Coefficient of linear thermal expansion |
x10-5/K |
ISO 11359-2 |
17.0 |
| Electrical property |
| Volume resistivity |
Ω・cm |
IEC 60093 |
1012 |
| Molding property |
| Mold shrinkage |
MD |
％ |
ISO 294-4 |
0.7 |
| TD |
1.4 |
| Other property |
| Density |
g/cm3 |
ISO 1183 |
1.01 |
| Water absorption |
equilibrium |
％ |
UBE method |
0.6 |