Dry as molded
  Unit Test method Measured value
Melting temperature °C  ISO 11357-3 195
Density g/cm3  ISO 1183-3 1.06
Tensile stress at yield MPa  ISO 527-1,2 30
Tensile strain at yield %  ISO 527-1,2 -
Tensile strain at break %  ISO 527-1,2 > 150
Flexural strength MPa  ISO 178 28
Flexural modulus MPa  ISO 178 700
Shore hardness D-scale -  ISO 868 -
Rockwell hardness R-scale -  ISO 2039-2 64
Impact strength (Charpy, Notched) 23 °C kJ/m2  ISO 179/1eA 80P
-40 °C kJ/m2  ISO 179/1eA 16C
Temp. of deflection under load 0.45 MPa °C  ISO 75-2 66
1.8 MPa °C  ISO 75-2 -
Moulding shrinkage (In flow direction/ In transverse direction) %  ISO 294-4 1.2/1.2
Abrasion loss (CS-17. 1,000 rev.) mg  ISO 9352 18
Coef. Of linear thermal expansion 10-4 /K  ISO 11359-2 1.0
Volume resistivity Ω·cm  IEC 60093 1014
Moisture absorption (24 h in water at 23 °C) %  ISO 62 1.4
Melt flow rate(250 °C/5,000 g) g/10 min  ISO 1133 6
Comments     Tubing
Impact modified
Color     Black

Impact Strength:N=not broken P=partially broken C=completely broken