Dry as molded
Characteristic Unit Test method Measured value
Mechanical Characteristics
Tensile stress at yield MPa  ISO 527-1,2 45
Tensile strain at break % > 50
Tensile modulus GPa 1.5
Flexural strength MPa  ISO 178 59
Flexural modulus GPa 1.5
Charpy notched impact strength kJ/m2  ISO 179-1/1eA 5
Rockwell hardness R.Scale -  ISO 2039-2 105
M.Scale -
Thermal Characteristics
Melting temperature °C  ISO 11357 175~181
Coeff. of linear thermal expansion x10-5/°C  ISO 11359-2 13
Temperature of deflection under load 0.45 MPa °C  ISO 75-1,2 90
1.8 MPa °C 45
Electical Characterisitics
Volume resistivity Ωcm  JIS K6911 1015
Electric strength kV/mm  IEC 60243-1 -
Relative permittivity -  IEC 60250 -
Arc resitance s  D-495(ASTM) -
Others
Density g/cm3  ISO 1183-3 1.02
Water absorption 23 °C, 50 %RH %  UBE method 0.7
Molding shrinkage MD %  UBE method(30x100x3t) 0.9
TD 1.2
Nomenclature accdording to ISO 16396-1 PA12, XH, C18-010