| Mechanical property |
| Tensile strength |
MPa |
ISO 527-1,2 |
225 |
| Tensile strain at break |
％ |
3 |
| Tensile modulus |
MPa |
15000 |
| Flexural strength |
MPa |
ISO 178 |
360 |
| Flexural modulus |
MPa |
14000 |
| Charpy notched impact strength |
kJ/m2 |
ISO 179-1/1eA |
19 |
| Tensile strength after moisture absorption |
MPa |
ISO 527-1,2 |
170 |
| Tensile modulus after moisture absorption |
MPa |
11000 |
| Tensile strain at break after moisture absorption |
％ |
4 |
| Flexural strength after moisture absorption |
MPa |
ISO 178 |
230 |
| Flexural modulus after moisture absorption |
MPa |
9000 |
| Charpy notched impact strength after moisture absorption |
J/m |
ISO 179-1/1eA |
26 |
| Rockwell hardness |
R.Scale |
- |
ISO 2039 |
120 |
| M.Scale |
105 |
| R.Scale(After Moisture absorption) |
115 |
| Thermal property |
| Melting temperature |
℃ |
ISO 11357 |
215～225 |
| Temperature of deflection under load |
0.45 MPa |
℃ |
ISO 75-1,2 |
220 |
| 1.8 MPa |
210 |
| Coefficient of linear thermal expansion |
x10-5/K |
ISO 11359-2 |
2.0 |
| Other property |
| Density |
g/cm3 |
ISO 1183 |
1.50 |
| Water absorption |
equilibrium |
％ |
UBE method |
1.3 |
| Flammability rating |
- |
UL94 |
HB |