| Mechanical property |
| Tensile strength |
MPa |
ISO 527-1,2 |
85 |
| Tensile strain at break |
％ |
17 |
| Tensile modulus |
MPa |
3200 |
| Flexural strength |
MPa |
ISO 178 |
110 |
| Flexural modulus |
MPa |
2800 |
| Charpy notched impact strength |
kJ/m2 |
ISO 179-1/1eA |
5 |
| Rockwell hardness |
R.Scale |
- |
ISO 2039 |
120 |
| M.Scale |
80 |
| R.Scale(After Moisture absorption) |
85 |
| Thermal property |
| Melting temperature |
℃ |
ISO 11357 |
215～225 |
| Temperature of deflection under load |
0.45 MPa |
℃ |
ISO 75-1,2 |
170 |
| 1.8 MPa |
60 |
| Electrical property |
| Arc resistance |
sec |
ASTM D495 |
122 |
| Comparative Tracking Index |
- |
UL 746A |
0 |
| Volume resistivity |
Ω・cm |
IEC 60093 |
1015 |
| Volume resistivity after moisture absorption |
1012 |