| Mechanical property |
| Tensile strength |
MPa |
ISO 527-1,2 |
200 |
| Tensile strain at break |
％ |
3 |
| Tensile modulus |
MPa |
12000 |
| Flexural strength |
MPa |
ISO 178 |
310 |
| Flexural modulus |
MPa |
10000 |
| Charpy notched impact strength |
kJ/m2 |
ISO 179-1/1eA |
15 |
| Tensile strength after moisture absorption |
MPa |
ISO 527-1,2 |
127 |
| Tensile modulus after moisture absorption |
MPa |
7500 |
| Tensile strain at break after moisture absorption |
% |
7 |
| Charpy notched impact strength after moisture absorption |
J/m |
ISO 179-1/1eA |
24 |
| Thermal property |
| Melting temperature |
℃ |
ISO 11357 |
215～225 |
| Temperature of deflection under load |
0.45 MPa |
℃ |
ISO 75-1,2 |
220 |
| 1.8 MPa |
210 |
| Coefficient of linear thermal expansion |
x10-5/K |
ISO 11359-2 |
2.0 |
| Molding property |
| Mold shrinkage |
MD |
％ |
ISO 294-4 |
0.2 |
| TD |
0.6 |
| Other property |
| Density |
g/cm3 |
ISO 1183 |
1.41 |