| Mechanical property |
| Tensile strength |
MPa |
ISO 527-1,2 |
80 |
| Tensile strain at break |
％ |
4 |
| Tensile modulus |
MPa |
3300 |
| Flexural strength |
MPa |
ISO 178 |
110 |
| Flexural modulus |
MPa |
2800 |
| Charpy notched impact strength |
kJ/m2 |
ISO 179-1/1eA |
5 |
| Rockwell hardness |
R.Scale |
- |
ISO 2039 |
120 |
| M.Scale |
85 |
| R.Scale(After Moisture absorption) |
85 |
| M.Scale(After Moisture absorption) |
55 |
| Thermal property |
| Melting temperature |
℃ |
ISO 11357 |
215～225 |
| Temperature of deflection under load |
0.45 MPa |
℃ |
ISO 75-1,2 |
165 |
| 1.8 MPa |
65 |
| Coefficient of linear thermal expansion |
x10-5/K |
ISO 11359-2 |
8.0 |
| Electrical property |
| Arc resistance |
sec |
ASTM D495 |
119 |
| Comparative Tracking Index |
- |
UL 746A |
0 |
| Volume resistivity |
Ω・cm |
IEC 60093 |
1015 |
| Volume resistivity after moisture absorption |
1012 |
| Molding property |
| Mold shrinkage |
MD |
％ |
ISO 294-4 |
1.0 |
| TD |
1.1 |
| Other property |
| Density |
g/cm3 |
ISO 1183 |
1.14 |
| Water absorption |
equilibrium |
％ |
UBE method |
2.5 |